Detailed Information on Publication Record
2015
Temperature Stability of AgCu Nanoparticles
SOPOUŠEK, Jiří, Ondřej ZOBAČ, Vít VYKOUKAL, Jiří BURŠÍK, Pavla ROUPCOVÁ et. al.Basic information
Original name
Temperature Stability of AgCu Nanoparticles
Authors
SOPOUŠEK, Jiří (203 Czech Republic, guarantor, belonging to the institution), Ondřej ZOBAČ (203 Czech Republic, belonging to the institution), Vít VYKOUKAL (203 Czech Republic, belonging to the institution), Jiří BURŠÍK (203 Czech Republic), Pavla ROUPCOVÁ (203 Czech Republic), Pavel BROŽ (203 Czech Republic, belonging to the institution), Jiří PINKAS (203 Czech Republic, belonging to the institution) and Jan VŘEŠŤÁL (203 Czech Republic, belonging to the institution)
Edition
Journal of Nanoparticle Research, 2015, 1388-0764
Other information
Language
English
Type of outcome
Článek v odborném periodiku
Field of Study
20000 2. Engineering and Technology
Country of publisher
Netherlands
Confidentiality degree
není předmětem státního či obchodního tajemství
Impact factor
Impact factor: 2.101
RIV identification code
RIV/00216224:14310/15:00081656
Organization unit
Faculty of Science
UT WoS
000368506700001
Keywords (in Czech)
Sintrace Mikroskopie Organokovy DSC KEMS
Keywords in English
Sintering Microscopy Organometallic DSC KEMS
Tags
Tags
International impact, Reviewed
Změněno: 5/3/2018 21:44, prof. RNDr. Jiří Pinkas, Ph.D.
V originále
The colloidal solutions of the Ag-Cu nanoparticles (NPs, 10-32 nm) were prepared by solvothermal reactions. The samples of dried AgCu NPs and the resulting microstructures after heat treatment in air were investigated by various methods including electron microscopy (TEM, SEM) and high-temperature X-ray powder diffraction (HTXRD). The AgCu randomly mixed, Cu-rich, and Ag-rich face centred cubic crystal lattices were detected during the experiments. The temperature induced sintering was observed experimentally by HTXRD at 250 degrees C. The phase transformations at high temperatures were monitored by differential scanning calorimetry. The formation of the Ag-rich grains during heating in air and evolution of copper oxide microstructure were detected.
In Czech
Koloidní roztoky nanočástic AgCu NPS (10-32 nm) byly připraveny solvotermální reakcemi. Vzorky sušené AgCu NP a výsledné mikrostruktury po tepelném zpracování na vzduchu byly zkoumány různými způsoby, včetně elektronové mikroskopie (TEM, SEM) a vysoké teploty X-ray práškové difrakce (XRD). AgCu náhodně smíchány, Cu-bohaté, a v průběhu experimentů bylo zjištěno Ag bohaté plošně centrovanou kubickou krystalovou mříže. Indukovaná slinovací teplota byla pozorována experimentálně HTXRD při 250? C. Fázové přeměny při vysokých teplotách byly sledovány pomocí diferenční skenovací kalorimetrií. bylo zjištěno tvorba Ag-bohaté zrna při zahřívání na vzduchu a vývoji oxidu mědi mikrostruktury.
Links
| ED1.1.00/02.0068, research and development project |
| ||
| GA14-12653S, research and development project |
|