BURŠÍK, Jiří, Ivo KUBĚNA, Vilma BURŠÍKOVÁ, Pavel SOUČEK, Lukáš ZÁBRANSKÝ, Saeed MIRZAEI a Petr VAŠINA. W-B-C Nanostructured Layers - Microstructure and Mechanical Properties. In Pavel Šandera. Material Structure & Micromechanics of Fracture VIII. 258. vyd. Švýcarsko: Trans Tech Publications. s. 416-419. ISBN 978-3-03835-626-4. doi:10.4028/www.scientific.net/SSP.258. 2017.
Další formáty:   BibTeX LaTeX RIS
Základní údaje
Originální název W-B-C Nanostructured Layers - Microstructure and Mechanical Properties
Autoři BURŠÍK, Jiří (203 Česká republika, garant), Ivo KUBĚNA (203 Česká republika), Vilma BURŠÍKOVÁ (203 Česká republika, domácí), Pavel SOUČEK (203 Česká republika, domácí), Lukáš ZÁBRANSKÝ (203 Česká republika, domácí), Saeed MIRZAEI (364 Írán, domácí) a Petr VAŠINA (203 Česká republika, domácí).
Vydání 258. vyd. Švýcarsko, Material Structure & Micromechanics of Fracture VIII, od s. 416-419, 4 s. 2017.
Nakladatel Trans Tech Publications
Další údaje
Originální jazyk angličtina
Typ výsledku Stať ve sborníku
Obor 10305 Fluids and plasma physics
Stát vydavatele Švýcarsko
Utajení není předmětem státního či obchodního tajemství
Forma vydání tištěná verze "print"
Kód RIV RIV/00216224:14310/17:00094609
Organizační jednotka Přírodovědecká fakulta
ISBN 978-3-03835-626-4
Doi http://dx.doi.org/10.4028/www.scientific.net/SSP.258
Klíčová slova anglicky coating; nanostructure; electron microscopy; nanoindentation; fracture toughness
Štítky NZ, rivok
Změnil Změnila: Ing. Nicole Zrilić, učo 240776. Změněno: 24. 3. 2018 19:53.
Anotace
Several W-B-C layers were prepared by magnetron sputtering. The microstructure of thin layers was observed by means of scanning and transmission electron microscopy on cross sections prepared using a focused ion beam. Both undisturbed layers and the volume under indentation prints were inspected. The W-B-C layers are fine nanostructured materials about 2 um thick and indents with loads up to 1 N do not cause any visible defects (cracks, delamination etc). The results were correlated with mechanical properties characterized by means of nanoindentation experiments in both the static and the dynamic loading regime using a Berkovich indenter. Elastic modulus, indentation hardness and fracture resistance of prepared nanostructured coatings were evaluated and discussed.
Návaznosti
GA15-17875S, projekt VaVNázev: Lokální mikrostrukturní změny vyvolané statickou a dynamickou indentací nanostrukturovaných a nanolaminovaných povlaků
Investor: Grantová agentura ČR, Lokální mikrostrukturní změny vyvolané statickou a dynamickou indentací nanostrukturovaných a nanolaminovaných povlaků
VytisknoutZobrazeno: 29. 3. 2024 11:39