AgNi core-shell nanoparticles by hot injection synthesis

VYKOUKAL, Vít a Jiří PINKAS. AgNi core-shell nanoparticles by hot injection synthesis. In NANOCON 2017 Brno, Czech Republic. 2017.

Základní údaje

• Originální název: AgNi core-shell nanoparticles by hot injection synthesis
• Název česky: Syntéza nanočástic AgNi core-shell metodou hot injection
• Autoři: VYKOUKAL, Vít (203 Česká republika, domácí) a Jiří PINKAS (203 Česká republika, garant, domácí).
• Vydání: NANOCON 2017 Brno, Czech Republic, 2017.

Další údaje

• Originální jazyk: angličtina
• Typ výsledku: Konferenční abstrakt
• Obor: 10402 Inorganic and nuclear chemistry
• Stát vydavatele: Česká republika
• Utajení: není předmětem státního či obchodního tajemství
• Kód RIV: RIV/00216224:14310/17:00098146
• Organizační jednotka: Přírodovědecká fakulta
• Klíčová slova česky: silver; nickel; core-shell; TEM/EDS; SAXS; phase separation; VSM
• Klíčová slova anglicky: stříbro; nikl; core-shell; TEM/EDS; SAXS; fázová separace; VSM
• Příznaky: Mezinárodní význam, Recenzováno

Anotace

Metal nanoalloys display many unusual properties, such as depression of melting point, plasmon resonance, catalytic activity, and phase separation. Nanoalloys can be prepared by a variety of synthetic approaches, but highly advantageous is the solvothermal synthesis, specifically in oleylamine (OA). Silver and nickel are mutually immiscible, but in the nanoform are in a very close contact and thus create atypical structures. AgNi nanoparticles were prepared by injection of a small volume of OA solution of AgNO3 and Ni(acac)2 in different molar ratios to a mixture of OA and octadecene at 230 °C. After 10 min, the reaction mixture was cooled down to room temperature and acetone was added to precipitate nanoparticles. The suspension was centrifuged and the precipitate was washed twice by a mixture of hexane and acetone. Finally, the precipitate was dispersed in hexane and characterized. Dynamic light scattering (DLS), transmission electron microscopy (TEM), elemental analyses (ICP OES), small-angle X-ray scattering (SAXS) and high-resolution TEM/STEM with EELS and EDS analyses were performed for determination of chemical composition, average size, size distribution and shape of the prepared nanoparticles. Elemental mapping of individual nanoparticles showed a core/shell structure in which the silver nucleus was covered by a nickel layer. HT-XRD together with VSM and SEM/EDX analysis prove the phase separation and reveal magnetic properties. Acknowledgements: This research has been financially supported by the Ministry of Education, Youth and Sports of the Czech Republic under the project CEITEC 2020 (LQ1601).

Návaznosti

• GA17-15405S, projekt VaV: Název: Pokročilé experimentální a teoretické přístupy k fázovým diagramům nanoslitin se zahrnutím vlivu velikosti částic

Investor: Grantová agentura ČR, Pokročilé experimentální a teoretické přístupy k fázovým diagramům nanoslitin se zahrnutím vlivu velikosti částic

• LM2015043, projekt VaV: Název: Česká infrastruktura pro integrativní strukturní biologii (Akronym: CIISB)

Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Czech Infrastructure for Integrative Structural Biology

• LQ1601, projekt VaV: Název: CEITEC 2020 (Akronym: CEITEC2020)

Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, CEITEC 2020