Synthesis and Characterization of the Ni, Au, and Pt Nanoparticles by Solvothermal and Borohydride ...
ZRUBCOVÁ, Galina and Jiří SOPOUŠEK. Synthesis and Characterization of the Ni, Au, and Pt Nanoparticles by Solvothermal and Borohydride Ways. 2017. |
Other formats:
BibTeX
LaTeX
RIS
|
Basic information | |
---|---|
Original name | Synthesis and Characterization of the Ni, Au, and Pt Nanoparticles by Solvothermal and Borohydride Ways |
Name in Czech | Syntéza a charakterizace Ni, Au a Pt nanočástic připravených solvotermálně a borhydridově |
Authors | ZRUBCOVÁ, Galina (703 Slovakia, guarantor, belonging to the institution) and Jiří SOPOUŠEK (203 Czech Republic, belonging to the institution). |
Edition | 2017. |
Other information | |
---|---|
Original language | English |
Type of outcome | Conference abstract |
Field of Study | 10403 Physical chemistry |
Country of publisher | Czech Republic |
Confidentiality degree | is not subject to a state or trade secret |
WWW | Nanocom 2017 Nanocom 2017 |
RIV identification code | RIV/00216224:14740/17:00095142 |
Organization unit | Central European Institute of Technology |
Keywords (in Czech) | nanočástice zlato nikl platina |
Keywords in English | anoparticle gold nickel platinum |
Tags | metalic, nanoparticles, nanočástice, rivok |
Tags | International impact |
Changed by | Changed by: Mgr. Pavla Foltynová, Ph.D., učo 106624. Changed: 28/3/2018 14:22. |
Abstract |
---|
The Ni, Au and Pt nanoparticles were prepared using (Ni(acac)2, HAuCl4 or H2PtCl6) precursors respectively. The precursor was dissolved in oleylamine and injected into preheated mixture of oleylamine and octadecene. The reaction mixture was cooled down to room temperature after time needed for nucleation and growth of nanoparticles. The nanoparticles were separated and purified. The metallic nanoparticles was stabilized in hexane and characterized. The alternative synthesis was reduction using NaBH4 in polar solvent. The precursors of gold or platinum were dissolved in water. The phase transferring agent was used for transfer of side products to organic solvent under intensive stirring. Organic phase was removed and NaBH4 was added. This mixture was stirring again to reduce PtIV into Pt0 or AuIV into Au0. Nanoparticles prepared by both methods were characterized by dynamic light scattering (DLS), transmission electron microscopy (TEM) in order to determinate average size, size distribution, stability and shape of the nanoparticles. Obtained results were discussed from the point of view of the size and stability. |
Abstract (in Czech) |
---|
Nanočástice Ni, Au a Pt byly připraveny za použití prekursorů (Ni (acac) 2, HAuCl4 nebo H2PtCl6). Prekurzor byl rozpuštěn v oleylaminu a injikován do předehřáté směsi oleylaminu a oktadecénu. Reakční směs byla po čase potřebná pro nukleaci a růst nanočástic ochlazena na pokojovou teplotu. Nanočástice byly odděleny a čištěny. Kovové nanočástice byly stabilizovány v hexanu a charakterizovány. Alternativní syntézou byla redukce za použití NaBH4 v polárním rozpouštědle. Prekurzory zlata nebo platiny byly rozpuštěny ve vodě. Prostředek pro přenos fáze byl použit pro přenos vedlejších produktů do organického rozpouštědla za intenzivního míchání. Organická fáze byla odstraněna a byl přidán NaBH4. Tato směs byla opět míchána za účelem snížení PtIV na PtO nebo AuIV na AuO. Nanočástice připravené oběma metodami byly charakterizovány dynamickým rozptylem světla (DLS), přenosovou elektronovou mikroskopií (TEM) za účelem stanovení průměrné velikosti, rozdělení velikosti, stability a tvaru nanočástic. Získané výsledky byly diskutovány z hlediska velikosti a stability. |
Links | |
---|---|
GA17-12844S, research and development project | Name: Tepelná a fázová stabilita pokročilých termoelektrických materiálů |
Investor: Czech Science Foundation | |
GA17-15405S, research and development project | Name: Pokročilé experimentální a teoretické přístupy k fázovým diagramům nanoslitin se zahrnutím vlivu velikosti částic |
Investor: Czech Science Foundation |
PrintDisplayed: 13/10/2024 14:00