Influence of electron beam irradiation on physical properties of microwave plasma synthesized graphene nanosheets

JURMANOVÁ, Jana, Ondřej JAŠEK, Jozef TOMAN, Miroslav ŠNÍRER and Michal KALINA. Influence of electron beam irradiation on physical properties of microwave plasma synthesized graphene nanosheets. Online. In Conference Proceedings - NANOCON 2019. 1st ed. Ostrava: TANGER Ltd., 2020, p. 85-90. ISBN 978-80-87294-95-6. Available from: https://dx.doi.org/10.37904/nanocon.2019.8453.

Basic information

• Original name: Influence of electron beam irradiation on physical properties of microwave plasma synthesized graphene nanosheets
• Name in Czech: Vliv ozáření elektronovým paprskem na fyzikální vlastnosti grafenových nanošupin připravených v mikrovlnném plazmatu
• Authors: JURMANOVÁ, Jana (203 Czech Republic, guarantor, belonging to the institution), Ondřej JAŠEK (203 Czech Republic, belonging to the institution), Jozef TOMAN (703 Slovakia, belonging to the institution), Miroslav ŠNÍRER (703 Slovakia, belonging to the institution) and Michal KALINA (203 Czech Republic).
• Edition: 1. vyd. Ostrava, Conference Proceedings - NANOCON 2019, p. 85-90, 6 pp. 2020.
• Publisher: TANGER Ltd.

Other information

• Original language: English
• Type of outcome: Proceedings paper
• Field of Study: 10305 Fluids and plasma physics
• Country of publisher: Czech Republic
• Confidentiality degree: is not subject to a state or trade secret
• Publication form: electronic version available online
• WWW: Web konference
• RIV identification code: RIV/00216224:14310/20:00114696
• Organization unit: Faculty of Science
• ISBN: 978-80-87294-95-6
• ISSN: 2694-930X
• Doi: http://dx.doi.org/10.37904/nanocon.2019.8453
• UT WoS: 000664115400013
• Keywords (in Czech): Grafen; elektronová mikroskopie; ozařování; struktura
• Keywords in English: Graphene; electron microscopy; irradiation; structure
• Tags: rivok
• Tags: International impact, Reviewed

Abstract

Scanning electron microscopy was used to determine physical properties of microwave plasma synthesized graphene nanosheets such as size and shape under various electron beam parameters (accelerating voltage, electron beam current, working distance). The stability and amount of defects of graphene nanosheets structure was investigated in dependence on these parameters and the results were compared to data obtained by TEM and Dynamic light scattering (DLS). Electron beam irradiation lead to change of nanosheets topography and defect formation was observed as well. The amorphization of the carbon nanostructure led to increase of intensity of D band (1360 cm-1) in Raman spectra. Contrary to electron beam irradiation damage the high temperature annealing, up to 800 °C, in Ar led to no observable changes.

Abstract (in Czech)

Ke stanovení fyzikálních vlastností syntetizované mikrovlnné plazmy byla použita rastrovací elektronová mikroskopie grafenové nanosheety, jako je velikost a tvar za různých parametrů elektronového paprsku (zrychlovací napětí, proud elektronového paprsku, pracovní vzdálenost). Stabilita a množství defektů grafenových nanočástic struktura byla zkoumána v závislosti na těchto parametrech a výsledky byly porovnány s údaji získané pomocí TEM a dynamického rozptylu světla (DLS). Ozařování elektronovým paprskem vedlo ke změně nanočástic byla také pozorována topografie a tvorba defektů. Amorfizace uhlíkové nanostruktury vedla k zvýšení intenzity pásma D (1360 cm-1) v Ramanových spektrech. Na rozdíl od poškození ozářením elektronovým paprskem vysokoteplotní žíhání, až 800 ° C, v Ar nevedlo k žádným pozorovatelným změnám.

Links

• GA18-08520S, research and development project: Name: Studium procesu nukleace dvourozměrných uhlíkových nanostruktur v mikrovlnném plazmatu

Investor: Czech Science Foundation

• LO1411, research and development project: Name: Rozvoj centra pro nízkonákladové plazmové a nanotechnologické povrchové úpravy (Acronym: CEPLANT plus)

Investor: Ministry of Education, Youth and Sports of the CR