Microstructural changes as postmortem temperature indicator in Ni-Co-Cr-Al-Y oxidation protection coatings
BAUFELD, Bernd, Marion BARTSCH, Pavel BROŽ and Martin SCHMÜCKERBasic information
Original name
Microstructural changes as postmortem temperature indicator in Ni-Co-Cr-Al-Y oxidation protection coatings
Name in Czech
Změny v mikrostruktuře jako dodatečný indikátor teploty v antioxidačním ochranném povlaku Ni-Co-Cr-Al-Y.
Authors
BAUFELD, Bernd (276 Germany), Marion BARTSCH (276 Germany), Pavel BROŽ (203 Czech Republic, guarantor) and Martin SCHMÜCKER (276 Germany)
Edition
Materials Science and Engineering A, Netherland, 2004, 0921-5093
Other information
Language
English
Type of outcome
Článek v odborném periodiku
Field of Study
10403 Physical chemistry
Country of publisher
Czech Republic
Confidentiality degree
není předmětem státního či obchodního tajemství
Impact factor
Impact factor: 1.445
RIV identification code
RIV/00216224:14310/04:00011651
Organization unit
Faculty of Science
UT WoS
000224489300019
Keywords in English
CALPHAD; Microstructure; Ni-Co-Cr-Al-Y; Phase equilibria; Precipitates; Temperature indicator
Změněno: 8/11/2004 16:20, doc. RNDr. Pavel Brož, Ph.D.
V originále
Microstructural changes in a metallic oxidation protection coating (Ni-Co-Cr-Al-Y) applied on a nickel base superalloy were investigated by means of scanning and transmission electron microscopy. The changes are due either to thermal mechanical fatigue testing under high thermal gradients or to defined isothermal heat treatments. The coated specimens were quenched from temperatures between 840 and 1100 C to ambient temperature. The resultant phases, their local distribution and compositions were determined by energy dispersive X-ray (EDX) spectroscopy and electron diffraction. Phase equilibria at respective temperatures were determined by thermodynamic calculations based on the CALPHAD method. The calculated and experimentally determined phase distributions were compared. A particular microstructural feature, namely the existence and spatial distribution of spherical gamma' Ni3Al precipitates in the coating and the diffusion zone between substrate and coating, was used as a postmortem indicator for the maximum temperature experienced by the specimen during testing. This paper gives a road map for developing a microstructural-based temperature calibration for complex metallic materials using thermodynamic simulations.
In Czech
Změny v mikrostruktuře kovového antioxidačního povlaku na bázi Ni-Co-Cr-Al-Y aplikovaného na slitinu na bázi niklu byly zkoumány prostřednictvím skenovací a transmisní elektronové mikroskopie. Změny byly dány vlivem teplotně-mechanické zátěže ve vysokém teplotním gradientu nebo vlivem čistě teplotního žíhání. Povlečený materiál byl zakalen z teploty 840 a 1000 C na teplotu místnosti. Výsledné fáze, jejich místní rozdělení a složení byly stanoveny prostřednictvím RTG spektroskopie a elektronové difrakce. Fázové rovnováhy při daných teplotách byly stanoveny pomocí termodynamických výpočtů založených na metodě CALPHAD. Vypočítaná a experimentálně stanovená rozdělení fází byla pak srovnána. Charakteristická podoba mikrostruktury, zvláště existence a zvláštní rozdělení kulovitých precipitátů fáze gamma' Ni3Al v povlaku a difúzní oblasti mezi substrátem a povlakem, byla použita pro dodatečné určení teplot, kterým byly vzorky vystaveny během testování.