FIKAR, Jan, Robert SCHALLER and Nadine BALUC. Mechanical spectroscopy of decagonal Al-Cu-Fe-Cr quasicrystalline coatings. Philosophical Magazine. ABINGDON OX14 4RN, OXON, ENGLAND: TAYLOR & FRANCIS LTD, 2004, vol. 84, No 33, p. 3571-3584. ISSN 1478-6435.
Other formats:   BibTeX LaTeX RIS
Basic information
Original name Mechanical spectroscopy of decagonal Al-Cu-Fe-Cr quasicrystalline coatings
Name in Czech Mechanická spektroskopie dekagonálních Al-Cu-Fe-Cr kvazikrystalických vrstev
Authors FIKAR, Jan (203 Czech Republic, guarantor), Robert SCHALLER (756 Switzerland) and Nadine BALUC (756 Switzerland).
Edition Philosophical Magazine, ABINGDON OX14 4RN, OXON, ENGLAND, TAYLOR & FRANCIS LTD, 2004, 1478-6435.
Other information
Original language English
Type of outcome Article in a journal
Field of Study 10302 Condensed matter physics
Country of publisher United Kingdom of Great Britain and Northern Ireland
Confidentiality degree is not subject to a state or trade secret
Impact factor Impact factor: 1.167
RIV identification code RIV/00216224:14310/04:00010997
Organization unit Faculty of Science
UT WoS 000224976900003
Keywords in English AL-PD-MN; PLASTIC-DEFORMATION; DISLOCATION-MOTION; INTERNAL-FRICTION; BEHAVIOR
Tags AL-PD-MN, behavior, DISLOCATION-MOTION, INTERNAL-FRICTION, PLASTIC-DEFORMATION
Changed by Changed by: Mgr. Jan Fikar, Ph.D., učo 7574. Changed: 14/2/2005 17:24.
Abstract
Mechanical spectroscopy measurements were performed on decagonal quasicrystalline Al-Cu-Fe-Cr coatings of three different thicknesses deposited on a mild steel substrate. The mechanical loss spectra indicate that the internal friction is mostly caused by the quasicrystalline coating and that the contributions of both the steel substrate and the interface are small. The shear modulus measured in torsion increases with temperature, while the Young's modulus measured in flexion behaves normally. This shear modulus anomaly is interpreted as being due to solid friction between cracked segments of the quasicrystalline coating. This phenomenon also explains the broad athermal maximum found to occur in isochronal internal friction measurements. A quantitative model successfully reproducing the observed behaviour has been developed. Finally, the reversible high-temperature exponential background was interpreted as being due to the onset of the brittle-to-ductile transition in the quasicrystalline coating. The measured activation enthalpy is similar to the value that was deduced from compression tests performed at high temperatures on icosahedral Al-Cu-Fe bulk material.
Abstract (in Czech)
Mechanická spektroskopie byla provedena na dekagonálních Al-Cu-Fe-Cr kvazikrystalických vrstvách o třech tloušťkách nanesených na ocelovém substrátu. Spektra mechanických ztrát ukazují, že vnitřní tření je způsobeno především kvazikrystalickou vrstvou, příspěvky od substrátu a rozhraní jsou malé. Smykový modul měřený v torzi roste s teplotou, zatímco Youngův modul ve flexi se chová normálně. Tato anomálie smykového modulu je interpretována jako suché tření mezi trhlinami v kvazikrystalické vrstvě. Toto též vysvětluje široké atermální maximum objevující se v isochronních měřeních vnitřního tření. Vytvořený kvantitativní model úspěšně reprodukuje pozorované chování. Též je pozorováno reverzibilní vysokoteplotní exponenciální pozadí, které je interpretováno jako počátek přechodu křehký-tvárný v kvazikrystalické vrstvě. Změřená aktivační entalpie je srovnatelná s hodnotou měřenou kompresním testem za vysoké teploty na ikosahedrálním Al-Cu-Fe.
Links
MSM 143100002, plan (intention)Name: Fyzikální vlastnosti nových materiálů a vrstevnatých struktur
Investor: Ministry of Education, Youth and Sports of the CR, Physical properties of new materials and layered structures
PrintDisplayed: 23/8/2024 08:33