| MÁLEK, J., F. HNILICA, J. VESELÝ, B. SMOLA, Sonia BARTÁKOVÁ a Jiří VANĚK. Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment. Materials Characterization. Elsevier, 2012, roč. 66, č. 1, s. 75-82. ISSN 1044-5803. Dostupné z: https://dx.doi.org/10.1016/j.matchar.2012.02.012. |
Další formáty:
BibTeX
LaTeX
RIS
@article{1071881,
author = {Málek, J. and Hnilica, F. and Veselý, J. and Smola, B. and Bartáková, Sonia and Vaněk, Jiří},
article_number = {1},
doi = {http://dx.doi.org/10.1016/j.matchar.2012.02.012},
keywords = {Titanium alloys; Mechanical properties; Aging; Light microscopy; Electron microscopy},
language = {eng},
issn = {1044-5803},
journal = {Materials Characterization},
title = {Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment},
url = {http://www.sciencedirect.com/science/article/pii/S104458031200037X},
volume = {66},
year = {2012}
}
TY - JOUR
ID - 1071881
AU - Málek, J. - Hnilica, F. - Veselý, J. - Smola, B. - Bartáková, Sonia - Vaněk, Jiří
PY - 2012
TI - Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment
JF - Materials Characterization
VL - 66
IS - 1
SP - 75-82
EP - 75-82
PB - Elsevier
SN - 10445803
KW - Titanium alloys
KW - Mechanical properties
KW - Aging
KW - Light microscopy
KW - Electron microscopy
UR - http://www.sciencedirect.com/science/article/pii/S104458031200037X
L2 - http://www.sciencedirect.com/science/article/pii/S104458031200037X
N2 - The influence of thermo-mechanical treatment on microstructure and mechanical properties of T-35Nb-6Ta has been studied. The thermo-mechanical treatment was chosen to correspond to the production of wire with suitable mechanical properties for dental implants. After casting the alloy was hot forged (700–900 degC), solution treated (850 degC/30 min, water quenched) and cold swaged (reductions up to 91%). The annealing (700 degC/3 h/furnace) or aging (450 degC/8 h/furnace) was used as final heat treatment. The microstructure was studied by using light microscopy, scanning electron microscopy, transmission electron microscopy and XRD analysis. Cold swaging introduces microstructure consisting of highly deformed Beta-phase grains with dislocation tangles and twins, which ensures high tensile strength about 820 MPa, low Young's modulus (~ 50 GPa) and good ductility ~ 10%. Subsequent aging increases tensile strength (1000 MPa) as well as Young's modulus (75 GPa) without diminishing ductility. Annealing at 700 degC slightly decreases tensile strength (730 MPa) and increases the ductility and Young's modulus (17% and 62 GPa respectively). The mechanical properties attained recommend the thermo-mechanical treatment for production of wires for dental implants.
ER -
MÁLEK, J., F. HNILICA, J. VESELÝ, B. SMOLA, Sonia BARTÁKOVÁ a Jiří VANĚK. Microstructure and mechanical properties of Ti-35Nb-6Ta alloy after thermomechanical treatment. \textit{Materials Characterization}. Elsevier, 2012, roč.~66, č.~1, s.~75-82. ISSN~1044-5803. Dostupné z: https://dx.doi.org/10.1016/j.matchar.2012.02.012.
|