Detailed Information on Publication Record
2014
Shear Strength of Copper Joints Prepared by Low Temperature Sintering of Silver Nanoparticles
PEŠINA, Zbyněk, Vít VYKOUKAL, Marian PALCUT and Jiří SOPOUŠEKBasic information
Original name
Shear Strength of Copper Joints Prepared by Low Temperature Sintering of Silver Nanoparticles
Name in Czech
Pevnost ve smyku měděných spojů připrených nízkoteplotní sintrací nanočástic stříbra
Authors
PEŠINA, Zbyněk (203 Czech Republic), Vít VYKOUKAL (203 Czech Republic, belonging to the institution), Marian PALCUT (703 Slovakia) and Jiří SOPOUŠEK (203 Czech Republic, guarantor, belonging to the institution)
Edition
Electronic Materials Letters, South Korea, Korean Inst Metals Materials, 2014, 1738-8090
Other information
Language
English
Type of outcome
Článek v odborném periodiku
Field of Study
20306 Audio engineering, reliability analysis
Country of publisher
Republic of Korea
Confidentiality degree
není předmětem státního či obchodního tajemství
References:
Impact factor
Impact factor: 1.980
RIV identification code
RIV/00216224:14740/14:00074924
Organization unit
Central European Institute of Technology
UT WoS
000330333300050
Keywords (in Czech)
Ag; Cu; shear strength; test; nanoparticle;
Keywords in English
Ag; Cu; pevnost ve smyku; zkouška; nanočástice;
Tags
International impact, Reviewed
Změněno: 11/3/2015 09:43, Martina Prášilová
V originále
In this work, mechanical properties of Cu-to-Cu joint samples prepared by low temperature sintering of Ag nanoparticle paste have been investigated. The silver nanopaste was prepared by a controlled thermal decomposition of an organometallic precursor. The as-synthesized Ag particles were spherical, with an average diameter of 8.5 nm. The Cu-to-Cu joint samples were made by placing a small amount of Ag nanopaste between two polished Cu plates and sintering at 150C, 200C, 220C and 350C in air. A normal load was applied to aid sintering. Mechanical properties were measured by imposing a uniform stress across the sample bond area and measuring the corresponding strain. The application of external load was found to have a positive effect on the material’s mechanical properties. Furthermore, interestingly high values of shear strength were observed.
In Czech
Byly zkoumány mechanické vlastnosti Cu-to-Cu spojů připravených nízkoteplotní sintrací pasty Ag nanočástic. Ag nanopasta byla připravena řízeným tepelným rozkladem organokovových prekurzorů. Syntetizované Ag NPs byly kulovité, o středním průměru 8,5 nm. Cu-to-Cu spoje byly vyrobeny umístěním malého množství Ag nanopasty mezi dvě leštěné Cu desky a sintrováním při 150C, 200C, 220C and 350C na vzduchu. Zatížení bylo použito na k podpoře sintrace. Mechanické vlastnosti byly měřeny stanovením napětí lomu a deformace. Bylo zjištěno, že aplikace vnějšího zatížení má pozitivní vliv na mechanické vlastnosti spoje.
Links
| ED1.1.00/02.0068, research and development project |
|