| BARTÁKOVÁ, Sonia, J. MALEK a Patrik PRACHÁR. The Effect of Oxygen Addition on Microstructure and Mechanical Properties of Various Beta-Titanium Alloys. JOM. WARRENDALE, PA 15086 USA: MINERALS METALS MATERIALS SOC, 2020, roč. 72, č. 4, s. 1656-1663. ISSN 1047-4838. Dostupné z: https://dx.doi.org/10.1007/s11837-019-03879-w. |
Další formáty:
BibTeX
LaTeX
RIS
@article{1650216,
author = {Bartáková, Sonia and Malek, J. and Prachár, Patrik},
article_location = {WARRENDALE, PA 15086 USA},
article_number = {4},
doi = {http://dx.doi.org/10.1007/s11837-019-03879-w},
keywords = {LOW YOUNGS MODULUS; ZR-O ALLOYS; PHASE-STABILITY; TENSILE PROPERTIES; TI-ALLOYS; TI-29NB-13TA-4.6ZR; SUPERELASTICITY; CORROSION; DESIGN},
language = {eng},
issn = {1047-4838},
journal = {JOM},
title = {The Effect of Oxygen Addition on Microstructure and Mechanical Properties of Various Beta-Titanium Alloys},
url = {https://link.springer.com/article/10.1007%2Fs11837-019-03879-w},
volume = {72},
year = {2020}
}
TY - JOUR
ID - 1650216
AU - Bartáková, Sonia - Malek, J. - Prachár, Patrik
PY - 2020
TI - The Effect of Oxygen Addition on Microstructure and Mechanical Properties of Various Beta-Titanium Alloys
JF - JOM
VL - 72
IS - 4
SP - 1656-1663
EP - 1656-1663
PB - MINERALS METALS MATERIALS SOC
SN - 10474838
KW - LOW YOUNGS MODULUS
KW - ZR-O ALLOYS
KW - PHASE-STABILITY
KW - TENSILE PROPERTIES
KW - TI-ALLOYS
KW - TI-29NB-13TA-4.6ZR
KW - SUPERELASTICITY
KW - CORROSION
KW - DESIGN
UR - https://link.springer.com/article/10.1007%2Fs11837-019-03879-w
L2 - https://link.springer.com/article/10.1007%2Fs11837-019-03879-w
N2 - Simultaneously achieving high strength and low Young's modulus is essential for implant materials due to the "stress-shielding effect". In this work, the mechanical properties and microstructure of various beta-titanium alloys based on the Ti-Nb system with additions of Zr, Ta and Sn have been studied. Those alloys were prepared via the arc melting process. Thermo-mechanical processing (i.e., hot forging, solution treatment and cold swaging) has been performed. The alloys exhibited low Young's modulus around 50 GPa (43 GPa was the lowest measured value) and tensile strength around 800 MPa. The tensile strength was increased via aging treatment (450 degrees C/8 h) to 985 MPa while the modulus increased to 75 GPa. On the other hand the addition of 0.4 wt.% of oxygen seems to be more beneficial as the tensile strength reached values as high as 1225 MPa and simultaneously maintained low Young's modulus (similar to 62 GPa) and sufficient elongation (similar to 8%).
ER -
BARTÁKOVÁ, Sonia, J. MALEK a Patrik PRACHÁR. The Effect of Oxygen Addition on Microstructure and Mechanical Properties of Various Beta-Titanium Alloys. \textit{JOM}. WARRENDALE, PA 15086 USA: MINERALS METALS MATERIALS SOC, 2020, roč.~72, č.~4, s.~1656-1663. ISSN~1047-4838. Dostupné z: https://dx.doi.org/10.1007/s11837-019-03879-w.
|