On thermal stability of nanocrystalline Ag–Cu-S powders
SOPOUŠEK, Jiří, Dáša DRENČAKOVÁ, Pavel BROŽ, Jiří BURŠÍK, Adéla ZEMANOVÁ et. al.Základní údaje
Originální název
On thermal stability of nanocrystalline Ag–Cu-S powders
Autoři
SOPOUŠEK, Jiří (203 Česká republika, garant, domácí), Dáša DRENČAKOVÁ (703 Slovensko, domácí), Pavel BROŽ (203 Česká republika, domácí), Jiří BURŠÍK, Adéla ZEMANOVÁ a Pavla ROUPCOVÁ
Vydání
Journal of Nanoparticle Research, Springer, 2021, 1388-0764
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10403 Physical chemistry
Stát vydavatele
Nizozemské království
Utajení
není předmětem státního či obchodního tajemství
Odkazy
Impakt faktor
Impact factor: 2.533
Kód RIV
RIV/00216224:14310/21:00119517
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000668540800001
Klíčová slova anglicky
Nanoparticles; Thermoelectrics; DSC; In situ XRPD; Stromayerite; Silver wires
Štítky
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 6. 1. 2022 13:10, Mgr. Marie Šípková, DiS.
Anotace
V originále
The nanocrystalline semiconducting compounds based on the AgCuS system are considered as low-cost candidates of thermoelectric materials with improved thermal stability. The nanocrystalline Ag–Cu—S powders were prepared from metal nitrates and sulphur powder in tetraethylene glycol (TEG) solvent by reductive agent NaBH4. The crystallite sizes of the observed phases were in the range between 60 and 80 nm. The chemical compositions of the as-received samples were analysed by the ICP-AES method and their phase compositions were evaluated by XRPD. The investigation was supplemented by DSC and in situ HTXRD thermal analysis. A more detailed in situ experiment was performed for a sample containing ternary phases. The nucleation and growth of silver micro-wires were first observed on the substrate involving ternary phases at isothermal heat treatment. The formation of silver wires and semi-conductive ternary thermoelectric phase (stromayerite τ3) is explained by observed phase transformation. The obtained results are complemented by microscopy (LM, SEM, TEM).