Feasibility of depth profiling of Zn-based coatings by laser ablation inductively coupled plasma optical emission and mass spectrometry using infrared Nd:YAG and ArF* lasers
HRDLIČKA, Aleš, Vítězslav OTRUBA, Karel NOVOTNÝ, Detlef GÜNTHER, Viktor KANICKÝ et. al.Základní údaje
Originální název
Feasibility of depth profiling of Zn-based coatings by laser ablation inductively coupled plasma optical emission and mass spectrometry using infrared Nd:YAG and ArF* lasers
Název česky
Možnosti hloubkového profilování zinkových vrstev laserovou ablací infračerveným Nd:YAG a ArF* laserem s indukčně vázaným plazmatem s optickou emisní a hmotnostně spektrometrickou detekcí
Autoři
HRDLIČKA, Aleš (203 Česká republika), Vítězslav OTRUBA (203 Česká republika), Karel NOVOTNÝ (203 Česká republika), Detlef GÜNTHER (276 Německo) a Viktor KANICKÝ (203 Česká republika, garant)
Vydání
Spectrochimica Acta Part B: Atomic Spectroscopy, Amsterdam, Elsevier, 2005, 0584-8547
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10402 Inorganic and nuclear chemistry
Stát vydavatele
Nizozemské království
Utajení
není předmětem státního či obchodního tajemství
Odkazy
Impakt faktor
Impact factor: 2.332
Kód RIV
RIV/00216224:14310/05:00013739
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000228853800006
Klíčová slova anglicky
Laser ablation; Inductively coupled plasma; Atomic emission spectrometry; Mass spectrometry; Depth profiling; Zinc coated sheet
Štítky
Změněno: 23. 5. 2005 11:27, Mgr. Aleš Hrdlička, Ph.D.
V originále
The feasibility of depth profiling of zinc-coated iron sheets by laser ablation (LA) was studied using an Nd:YAG laser (1064 nm) with inductively coupled plasma optical emission spectrometry (ICP-OES), and an excimer ArF* laser (193 nm) with a beam homogenizer. The latter was coupled to an ICP with mass spectrometry (ICP-MS). Fixed-spot ablation was applied. Both LA systems were capable of providing depth profiles that approach the profiles obtained by glow discharge optical emission spectroscopy (GD-OES) and electron probe X-ray microanalysis (EPXMA). For Nd:YAG laser an artefact consisting in zinc depth profile signal tailing appeared, enlarging thus erroneously diffusional coating-substrate interface profile. However, the ArF* system partially reduced but not suppressed that phenomenon. For both LA systems the Fe signal from the substrate increased with depth as expected and reached a plateau. The depth resolution (depth range corresponding to 84-16% change in the full signal) achieved was several micrometers. Ablation rate was found to depend on ablation spot area at constant irradiance. Consequently, ablated volume per shot dependence on pulse energy exhibits deviation from linear course.
Česky
Byly měřeny hloubkové profily pozinkovaných ocelových plechů laserovou ablací (LA) Nd:YAG (1064 nm) s indukčně vázaným plazmatem a optickou emisní detekcí (ICP-OES)a excimerovým ArF* laserem (193 nm)s hmotnostní spektrometrickou detekcí (ICP-MS). Ablatovalo se do bodu a oba systémy naměřily podobné profily jako optický emisní spektrometr s doutnavým výbojem (GD-OES) a elektronová mikrosonda (EPXMA). Profil z Nd:YAG laseru byl nadměrně rozšířen přetrvávajícím signálem ze zinkové vrstvy. Tento jev však byl jen částečně potlačen, ale nikoliv odstraněn použitím ArF* laseru. U obou systémů signál železa rostl podle očekávání, až dosáhl plato. Hloubkové rozlišení (hloubkový interval, v němž se max. signál změní z 84%-16%) bylo několik mikrometrů. Ablační rychlost závisela na velikosti ablatované plochy při konstantní hustotě výkonu, tzn., že ablatovaný objem jedním pulzem vykazoval odchylky od lineární závislosti na energii pulzu.