Surface modification of polycarbonate in homogeneous atmospheric pressure discharge
ŠÍRA, Martin, David TRUNEC, Pavel SŤAHEL, Vilma BURŠÍKOVÁ, Zdeněk NAVRÁTIL et. al.Základní údaje
Originální název
Surface modification of polycarbonate in homogeneous atmospheric pressure discharge
Název česky
Úprava povrchu polykarbonátu v homogenním výboji za atmosférického tlaku
Autoři
ŠÍRA, Martin (203 Česká republika, garant), David TRUNEC (203 Česká republika), Pavel SŤAHEL (203 Česká republika), Vilma BURŠÍKOVÁ (203 Česká republika) a Zdeněk NAVRÁTIL (203 Česká republika)
Vydání
Journal of Physics D: Applied physics, 2007, 0022-3727
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10305 Fluids and plasma physics
Stát vydavatele
Velká Británie a Severní Irsko
Utajení
není předmětem státního či obchodního tajemství
Impakt faktor
Impact factor: 2.200
Kód RIV
RIV/00216224:14310/07:00020682
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000253177300023
Klíčová slova anglicky
homogeneous atmospheric pressure discharge; polycarbonate; surface free energy
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 18. 12. 2007 15:43, Mgr. Martin Šíra, Ph.D.
V originále
A homogeneous atmospheric pressure dielectric barrier discharge was used for the surface modification of polycarbonate (PC). The discharge was generated between two planar metal electrodes, the top electrode was covered by glass and the bottom electrode was covered by a polymer sample. The discharge burned in pure nitrogen or in a mixture of nitrogen and hydrogen. The surface properties of both treated and untreated polymers were characterized by atomic force microscopy, surface free energy (SFE) measurements and x-ray photoelectron spectroscopy. The influence of the treatment time and power input to the discharge on the surface properties of polymers was studied. The ageing of treated samples was also investigated. The treatment of polymers in the homogeneous atmospheric pressure discharge was homogeneous and the polymer surfaces showed a smaller degree of roughness in comparison with the polymer surfaces treated in a filamentary discharge. The SFE of the treated PC obtained at optimum conditions was 53 mJ cm-2 and the corresponding contact angle of water was 38deg . The maximum decrease in the SFE during ageing was about 13%. The analysis of the chemical composition showed an increase in the nitrogen concentration in the surface layer, but almost a zero increase in the oxygen concentration. This result was discussed concerning the measured values of the SFE measurement.
Česky
Úprava povrchu polykarbonátu v homogenním výboji za atmosférického tlaku
Návaznosti
| GA202/06/1473, projekt VaV |
| ||
| MSM0021622411, záměr |
|