Nanoscopic Cobalt Ferrite by Sonolysis of M(acac)3 Complexes

OSTŘÍŽEK, Petr, Jiří PINKAS, Radek ZBOŘIL, Zdeněk MORAVEC a Petr BEZDIČKA. Nanoscopic Cobalt Ferrite by Sonolysis of M(acac)3 Complexes. In 11 th Meeting of the European Society of Sonochemistry. 1. vyd. Basancon, Francie: UTINAM Universite de Franche-Comte, 2008, s. 181-182. ISSN 1350-4177.

Základní údaje

• Originální název: Nanoscopic Cobalt Ferrite by Sonolysis of M(acac)3 Complexes
• Název česky: Příprava nanoskopického kobaltnatého ferritu sonolýzou komplexů M(acac)3
• Autoři: OSTŘÍŽEK, Petr (203 Česká republika), Jiří PINKAS (203 Česká republika, garant), Radek ZBOŘIL (203 Česká republika), Zdeněk MORAVEC (203 Česká republika) a Petr BEZDIČKA (203 Česká republika).
• Vydání: 1. vyd. Basancon, Francie, 11 th Meeting of the European Society of Sonochemistry, od s. 181-182, 2 s. 2008.
• Nakladatel: UTINAM Universite de Franche-Comte

Další údaje

• Originální jazyk: angličtina
• Typ výsledku: Stať ve sborníku
• Obor: 10402 Inorganic and nuclear chemistry
• Stát vydavatele: Francie
• Utajení: není předmětem státního či obchodního tajemství
• Impakt faktor: Impact factor: 2.796
• Kód RIV: RIV/00216224:14310/08:00026052
• Organizační jednotka: Přírodovědecká fakulta
• ISSN: 1350-4177
• Klíčová slova anglicky: Sonochemistry; Iron; Cobalt; Oxides; Ferrite; Nanoparticles
• Štítky: cobalt, Ferrite, Iron, nanoparticles, Oxides, Sonochemistry
• Příznaky: Mezinárodní význam, Recenzováno

Anotace

We examined the sonochemical synthesis of CoFe2O4. Composite nanoscopic particles consisting of Co-Fe oxide particles and an organic matrix were prepared by sonolysis of mixtures of 2,4-pentanedionato complexes, M(acac)n, M = Fe, Co; n = 2, 3. The XRD results showed that phase pure CoFe2O4 samples were prepared with a molar content of Co:Fe from 1:1.3 to 1:2.0. Addition of variable amounts of water was found to facilitate the decomposition of precursor complexes. That allowed control of the organics content and the BET surface area of the oxide nanoparticles. Powders with specific surface area as high as 218 m2 g-1 were obtained. FE-SEM was used to examine particle shape, size, and size distribution with an estimated diameter of 20-30 nm. Variable temperature XRD also revealed the spinel crystallization on heating. A small particle size below 20 nm of the crystalline CoFe2O4 is retained up to 600 oC.

Anotace česky

Studium přípravy nanoskopického kobaltnatého ferritu CoFe2O4 sonolýzou komplexů M(acac)n, M = Fe, Co; n = 2, 3.