Experimental and theoretical studies of bainitic creep-resisting T23 steel

SVOBODOVÁ, Marie a Jiří SOPOUŠEK. Experimental and theoretical studies of bainitic creep-resisting T23 steel. In CALPHAD XXXVIII (May 17-22, 2009). 2009.

Základní údaje

Originální název

Experimental and theoretical studies of bainitic creep-resisting T23 steel

Název česky

Experimentální a teoretická studie bainitických creepově odolných T23 ocelí

Název anglicky

Experimental and theoretical studies of bainitic creep-resisting T23 steel

Autoři

SVOBODOVÁ, Marie (203 Česká republika, garant) a Jiří SOPOUŠEK (203 Česká republika, domácí)

Vydání

CALPHAD XXXVIII (May 17-22, 2009), 2009

---

Další údaje

Jazyk

čeština

Typ výsledku

Konferenční abstrakt

Obor

10403 Physical chemistry

Stát vydavatele

Slovensko

Utajení

není předmětem státního či obchodního tajemství

Kód RIV

RIV/00216224:14310/09:00051151

Organizační jednotka

Přírodovědecká fakulta

Klíčová slova česky

CALPHAD; svar; fázové diagramy; ocel

Klíčová slova anglicky

CALPHAD; weld; phase diagram; steel

Štítky

CALPHAD, IK, Phase diagram, rivok, steel, weld

Příznaky

Mezinárodní význam

---

Anotace

V originále

CALPHAD approach is a progressive tool of material engineering helping in a development of new advanced materials. Based on this approach, we can make phase diagram calculations and predictions, and simulate diffusion-controlled phase transformation, too. In a view of the application, these phase diagrams calculations play a significant role in a, i.e., prediction of thermal-induced structure changes in new materials supposed to be used for power industry. Furthermore, perhaps all structural parts of power plants are welded, so, if the operation temperature is achieving values above 500stC, the simulations of diffusion-controlled phase transformations occurring in so thermal loaded weld joints enable to predict their structure stability and then a service lifetime of all the structural part. One of those new materials supposed to be used for power industry is bainitic creep-resisting T23 steel, a modification of low-alloyed 2.25Cr-1Mo steel, containing Cr (2.25 wt.%), Mo (0.1 wt.%), C, V, Mn (each 0.2 wt.%), and B, N (each 0.006 wt.%). Moreover, T23 steel is alloyed with 1.6 wt.% of W and 0.04 wt.% of Nb. Due to addings, as-treated steel has an improved creep resistance, high elastic-plastic properties, and a good weldability. Therefore, T23 steel is said to be use for power components at operating conditions up to 600degC. Because of, considering a service lifetime of components, a necessary prediction of long-term structure, corrosion, and strength behaviour of the material, our research was focused on study of structure behaviour of T23 steel at long-term isothermal exposure at 650degC. In opposite to 100 000 hrs exposure at 600stC (maximum service temperature), the increased temperature allows to get same degraded structure of steel after already 10 000 hrs. The thermal-induced phase transformations of as-received, as-welded, and as-exposed T23 steel were predicted by using Thermo-Calc and DICTRA. At the same time, XRD analysis, light and electron microscopy, and Vickers hardness measurement were used.

Anglicky

CALPHAD approach is a progressive tool of material engineering helping in a development of new advanced materials. Based on this approach, we can make phase diagram calculations and predictions, and simulate diffusion-controlled phase transformation, too. In a view of the application, these phase diagrams calculations play a significant role in a, i.e., prediction of thermal-induced structure changes in new materials supposed to be used for power industry. Furthermore, perhaps all structural parts of power plants are welded, so, if the operation temperature is achieving values above 500stC, the simulations of diffusion-controlled phase transformations occurring in so thermal loaded weld joints enable to predict their structure stability and then a service lifetime of all the structural part. One of those new materials supposed to be used for power industry is bainitic creep-resisting T23 steel, a modification of low-alloyed 2.25Cr-1Mo steel, containing Cr (2.25 wt.%), Mo (0.1 wt.%), C, V, Mn (each 0.2 wt.%), and B, N (each 0.006 wt.%). Moreover, T23 steel is alloyed with 1.6 wt.% of W and 0.04 wt.% of Nb. Due to addings, as-treated steel has an improved creep resistance, high elastic-plastic properties, and a good weldability. Therefore, T23 steel is said to be use for power components at operating conditions up to 600degC. Because of, considering a service lifetime of components, a necessary prediction of long-term structure, corrosion, and strength behaviour of the material, our research was focused on study of structure behaviour of T23 steel at long-term isothermal exposure at 650degC. In opposite to 100 000 hrs exposure at 600stC (maximum service temperature), the increased temperature allows to get same degraded structure of steel after already 10 000 hrs. The thermal-induced phase transformations of as-received, as-welded, and as-exposed T23 steel were predicted by using Thermo-Calc and DICTRA. At the same time, XRD analysis, light and electron microscopy, and Vickers hardness measurement were used.