Study of Sn Sb Zn Ternary System

ULICHOVÁ, Alena, Ondřej ZOBAČ a Jiří SOPOUŠEK. Study of Sn Sb Zn Ternary System. In CALPHAD XXXVIII (May 17-22, 2009). 2009.

Základní údaje

• Originální název: Study of Sn Sb Zn Ternary System
• Název česky: Studium ternární soustavy Sn Sb Zn
• Název anglicky: Study of Sn Sb Zn Ternary System
• Autoři: ULICHOVÁ, Alena (203 Česká republika, garant, domácí), Ondřej ZOBAČ (203 Česká republika, domácí) a Jiří SOPOUŠEK (203 Česká republika, domácí).
• Vydání: CALPHAD XXXVIII (May 17-22, 2009), 2009.

Další údaje

• Originální jazyk: čeština
• Typ výsledku: Konferenční abstrakt
• Obor: 10403 Physical chemistry
• Stát vydavatele: Slovensko
• Utajení: není předmětem státního či obchodního tajemství
• Kód RIV: RIV/00216224:14310/09:00051153
• Organizační jednotka: Přírodovědecká fakulta
• Klíčová slova česky: CALPHAD; termická analýza; fázové diagramy
• Klíčová slova anglicky: CALPHAD; thermal analysis; phase diagram
• Štítky: CALPHAD, IK, Phase diagram, rivok, Thermal analysis
• Příznaky: Mezinárodní význam

Anotace

The CALPHAD method [1] was used for preliminary phase diagram calculations using thermodynamic database COST 531 [2] optimized for lead-free solders. The preliminary phase diagram cross-sections were respected in alloy preparation so that the compositions of the alloys were in different phase fields. The zinc composition varied approximately from 2 to 20 wt % and antimony from 6 to 75wt%. The alloys were annealed and after that investigated by light microscopy. The compositions of the equilibrated phases were obtained by means of EDX microanalysis. Thermal effects during melting and solidifying were experimentally studied by the DSC technique in the inert atmosphere using the different heating and cooling rates 1-10K/min. The liquidus and solidus were determined. The DSC signal was also simulated by method similar to approach given in literature [3]. The experimental DSC signal of each alloy was compared with a simulated curve. The experimental temperatures of phase transformations were found.

Anotace anglicky

The CALPHAD method [1] was used for preliminary phase diagram calculations using thermodynamic database COST 531 [2] optimized for lead-free solders. The preliminary phase diagram cross-sections were respected in alloy preparation so that the compositions of the alloys were in different phase fields. The zinc composition varied approximately from 2 to 20 wt % and antimony from 6 to 75wt%. The alloys were annealed and after that investigated by light microscopy. The compositions of the equilibrated phases were obtained by means of EDX microanalysis. Thermal effects during melting and solidifying were experimentally studied by the DSC technique in the inert atmosphere using the different heating and cooling rates 1-10K/min. The liquidus and solidus were determined. The DSC signal was also simulated by method similar to approach given in literature [3]. The experimental DSC signal of each alloy was compared with a simulated curve. The experimental temperatures of phase transformations were found.

Návaznosti

• MSM0021622410, záměr: Název: Fyzikální a chemické vlastnosti pokročilých materiálů a struktur

Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Fyzikální a chemické vlastnosti pokročilých materiálů a struktur

• OC09010, projekt VaV: Název: Studium termodynamických vlastností a fázových diagramů soustav pro vysokoteplotní bezolovnaté pájky

Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Studium termodynamických vlastností a fázových diagramů soustav pro vysokoteplotní bezolovnaté pájky