Sonochemical Synthesis of Amorphous Yttrium Iron Oxides Embedded in Acetate Matrix and their Controlled Thermal Crystallization toward Garnet (Y3Fe5O12) and Perovskite (YFeO3) Nanostructures
PINKAS, Jiří, Vendula REICHLOVÁ, Aneta SERAFIMIDISOVÁ, Zdeněk MORAVEC, Radek ZBOŘIL et. al.Základní údaje
Originální název
Sonochemical Synthesis of Amorphous Yttrium Iron Oxides Embedded in Acetate Matrix and their Controlled Thermal Crystallization toward Garnet (Y3Fe5O12) and Perovskite (YFeO3) Nanostructures
Název česky
Sonochemická syntéza amorfních oxidů yttrito-železitých v acetátové matrici a jejich řízená termická krystalizace na granátové (Y3Fe5O12) a perovskitové (YFeO3) nanostruktury
Autoři
PINKAS, Jiří (203 Česká republika, garant, domácí), Vendula REICHLOVÁ (203 Česká republika), Aneta SERAFIMIDISOVÁ (203 Česká republika), Zdeněk MORAVEC (203 Česká republika, domácí), Radek ZBOŘIL (203 Česká republika), Dalibor JANČÍK (203 Česká republika) a Petr BEZDIČKA (203 Česká republika)
Vydání
JOURNAL OF PHYSICAL CHEMISTRY C, WASHINGTON, AMER CHEMICAL SOC, 2010, 1932-7447
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10402 Inorganic and nuclear chemistry
Stát vydavatele
Spojené státy
Utajení
není předmětem státního či obchodního tajemství
Impakt faktor
Impact factor: 4.524
Kód RIV
RIV/00216224:14310/10:00044673
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000280727500022
Klíčová slova česky
sonochemie; nanočástice; amorfní; oxid yttrito-železitý; granát; perovskit
Klíčová slova anglicky
Sonochemistry; Nanoparticles; Amorphous; Yttrium Iron Oxide; Garnet; Perovskite
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 31. 1. 2011 16:46, prof. RNDr. Jiří Pinkas, Ph.D.
V originále
Sonolysis of stoichiometric mixtures of tris(2,4 pentanedionato)iron, Fe(acac)3, and tris(2,4-pentanedionato) yttrium, Y(acac)3(H2O)3, under Ar atmosphere in tetraglyme led to a colloidal solution from which amorphous Y-Fe-O nanopowders could be precipitated by hexane. These powders are composed of amorphous nanoparticles (3 nm) of yttrium iron(III) oxide embedded in an acetate matrix as proved by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), mass spectrometry, and Mossbauer and IR spectroscopy. The thermally induced crystallization of the amorphous Y-Fe-O nanoparticles was studied by thermal analysis (TG/ DSC), evolved gas analysis (EGA), high-temperature XRD, and Mossbauer spectroscopy. Depending on the Y/Fe starting stoichiometric ratio in the sonicated reaction mixture, the single-phase YFeO3 (YIP) with the perovskite structure or Y3Fe5O12 (YIG) with the garnet structure can be synthesized by such controlled thermal transformation.
Česky
Sonolýza stochiometrických směsí tris(2,4 pentanedionato)železitého komplexu, Fe(acac)3, a tris(2,4-pentanedionato) yttritého komplexu, Y(acac)3(H2O)3, v Ar atmosféře v tetraglymu poskytla koloidní roztok, ze kterého se vyloučily amorfní Y-Fe-O nanoprášky skládajicí se z nanočástic (3 nm) oxidu yttrito-železitého v v acetátové matrici, což bylo potvrzeno pomocí rtg. difrakce (XRD), transmisní elektronové mikroskopie (TEM), skenovací elektronové mikroskopie (SEM), hmotnostní spektrometrie, a Mossbauerovy a IR spektroskopie. Termicky indukovaná krystalizace amorfních Y-Fe-O nanočástic byla studována pomocí termické analýzy (TG/ DSC), EGA, HT-XRD, a Mossbauerovy spektroskopie. V závislosti na výchozím poměru Y/Fe byly získány nanočástice YFeO3 (YIP) perovskitu nebo Y3Fe5O12 (YIG) granátu.