Air DCSBD plasma treatment of Al surface at atmospheric pressure
PRYSIAZHNYI, Vadym, Petr VAŠINA, Nagender Reddy PANYALA, Josef HAVEL, Mirko ČERNÁK et. al.Základní údaje
Originální název
Air DCSBD plasma treatment of Al surface at atmospheric pressure
Autoři
PRYSIAZHNYI, Vadym (804 Ukrajina, garant, domácí), Petr VAŠINA (203 Česká republika, domácí), Nagender Reddy PANYALA (356 Indie, domácí), Josef HAVEL (203 Česká republika, domácí) a Mirko ČERNÁK (703 Slovensko, domácí)
Vydání
Surface and Coatings Technology, 2012, 0257-8972
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10305 Fluids and plasma physics
Stát vydavatele
Švýcarsko
Utajení
není předmětem státního či obchodního tajemství
Odkazy
Impakt faktor
Impact factor: 1.941
Kód RIV
RIV/00216224:14310/12:00057287
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000301017300040
Klíčová slova česky
Aluminum; Atmospheric pressure plasma; Surface treatment
Klíčová slova anglicky
Aluminum; Atmospheric pressure plasma; Surface treatment
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 22. 4. 2013 14:14, Ing. Andrea Mikešková
V originále
The ambient air plasma cleaning and activation effects on aluminum surface using the Diffuse Coplanar Surface Barrier Discharge in ambient air are presented. Atomic Force Microscopy, Attenuated Total Reflectance FTIR and Laser Desorption/Ionization Time-of-Flight Mass Spectroscopy techniques were used to characterize the changes on the surface before and after plasma treatments. The plasma cleaning effect on aluminum, i.e. decrease of hydrocarbon contamination, was proven. Also the air plasma treatment resulted in a significant increase of amount of OH groups on the surface and in a decrease of the surface roughness.
Česky
The ambient air plasma cleaning and activation effects on aluminum surface using the Diffuse Coplanar Surface Barrier Discharge in ambient air are presented. Atomic Force Microscopy, Attenuated Total Reflectance FTIR and Laser Desorption/Ionization Time-of-Flight Mass Spectroscopy techniques were used to characterize the changes on the surface before and after plasma treatments. The plasma cleaning effect on aluminum, i.e. decrease of hydrocarbon contamination, was proven. Also the air plasma treatment resulted in a significant increase of amount of OH groups on the surface and in a decrease of the surface roughness.