SILVER NANOPARTICLES SINTERING AT LOW TEMPERATURE ON A COPPER SUBSTRATE: IN SITU CHARACTERISATION UNDER INERT ATMOSPHERE AND AIR
SOPOUŠEK, Jiří, Jiří BURŠÍK, Jakub ZÁLEŠÁK a Zbyněk PEŠINAZákladní údaje
Originální název
SILVER NANOPARTICLES SINTERING AT LOW TEMPERATURE ON A COPPER SUBSTRATE: IN SITU CHARACTERISATION UNDER INERT ATMOSPHERE AND AIR
Název česky
Nizkoteplotní sintrace nanostříbra na substrátu mědi: In situ charakterizace za inertní atmosféry a na vzduchu
Autoři
SOPOUŠEK, Jiří (203 Česká republika, garant, domácí), Jiří BURŠÍK (203 Česká republika), Jakub ZÁLEŠÁK (203 Česká republika, domácí) a Zbyněk PEŠINA (203 Česká republika)
Vydání
Journal of Mining and Metallurgy B, Bor, Serbia, Faculty of Metallurgy, Bor, 2012, 1450-5339
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
20000 2. Engineering and Technology
Stát vydavatele
Srbsko
Utajení
není předmětem státního či obchodního tajemství
Impakt faktor
Impact factor: 1.435
Kód RIV
RIV/00216224:14740/12:00057393
Organizační jednotka
Středoevropský technologický institut
UT WoS
000300798900007
Klíčová slova česky
Thermal analysis; Silver; copper; DSC; electrical resistance; heat of sintering
Klíčová slova anglicky
Termická analýza; stříbro; měď; DSC; elektrická vodivost; teplo sintrace
Štítky
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 12. 4. 2013 09:15, Olga Křížová
V originále
Silver nanoparticles (Ag-NPs) were prepared by wet synthesis. The Ag-NPs suspension and the copper substrate plate were used for a preparation of substrate-nanoparticle-substrate samples. The sandwich like samples Cu/Ag/Cu were prepared and investigated in-situ at the isothermal external conditions (IEC) and inside apparatus for simultaneous thermal analysis STA409. The in-situ results of the electrical resistance were recorded during the Cu/Ag/Cu (IEC) sample preparation and heat treatment. Thermal effects of the Ag-NPs sintering between copper substrates were measured by differential scanning calorimetry (DSC) under different atmospheres. The prepared Cu/Ag/Cu sandwich samples were characterised by means of both optical and electron microscopy. The process of the low temperature sintering of the Ag-NPs was monitored using both thermogravimetry (TG) and DSC technique inside calorimeter under inert gas and under synthetic air. The exothermic heat effect of nanosilver sintering was evaluated.
Česky
Ag nano bylo připraveno mokrou syntézou. Byly připraveny sendvičové vzorky Cu/AG-NANO/Cu. Byl měřen tepelný efekt sintrace v DSC metodou v kalorimetru. Sintrace byla sledována pod inertním plynem a v argonu.