MÁLEK, J., F. HNILICA, J. VESELÝ, B. SMOLA, Sonia BARTÁKOVÁ a Jiří VANĚK. The influence of chemical composition and thermo-mechanical treatment on Ti–Nb–Ta–Zr alloys. Materials and Design. Nizozemsko, 2012, roč. 35, č. 3, s. 731-740. ISSN 0261-3069. Dostupné z: https://dx.doi.org/10.1016/j.matdes.2011.10.030.
Další formáty:   BibTeX LaTeX RIS
Základní údaje
Originální název The influence of chemical composition and thermo-mechanical treatment on Ti–Nb–Ta–Zr alloys
Název česky Vliv chemického složení a termomechanického ovlivnění na slitinu Ti–Nb–Ta–Zr
Autoři MÁLEK, J., F. HNILICA, J. VESELÝ, B. SMOLA, Sonia BARTÁKOVÁ a Jiří VANĚK.
Vydání Materials and Design, Nizozemsko, 2012, 0261-3069.
Další údaje
Originální jazyk angličtina
Typ výsledku Článek v odborném periodiku
Obor 30200 3.2 Clinical medicine
Stát vydavatele Nizozemské království
Utajení není předmětem státního či obchodního tajemství
Impakt faktor Impact factor: 2.913
Organizační jednotka Lékařská fakulta
Doi http://dx.doi.org/10.1016/j.matdes.2011.10.030
UT WoS 000301578700090
Klíčová slova česky termomechanické ovlivnění; mikrostrukturní změny; mechanické vlastnosti
Klíčová slova anglicky Thermo mechanical treatment; Microstructural changes; Mechanical properties
Příznaky Mezinárodní význam
Změnil Změnila: Ing. Mgr. Věra Pospíšilíková, učo 9005. Změněno: 23. 4. 2013 07:40.
Anotace
Ti–Nb–Ta–Zr quaternary alloying system is very promising for biomedical alloys. It is due to good mechanical properties and corrosion resistance of titanium alloys. Moreover no potentially harmful elements are contained in this system. Mechanical properties were influenced by changing the chemical composition and by various heat-treatment operations. The alloys were prepared by arc melting and then they were hot forged (900–1000 degC). After solution treatment 850 degC/0.5 h/water quenched, cold swaging was carried out with section reduction about 85%. As final heat treatment aging at 450 degC/8 h/furnace cooling was used. Mechanical properties were measured from tensile tests results at cold swaged and aged specimens. The microstructure was observed by using light microscopy and transmission electron microscopy (TEM)-thin foils method. X-ray diffraction analysis reveals the phase composition. By using these techniques the changes in microstructure caused by precipitation during aging treatment were clarified. After aging, the presence of phases may occur. Influence of changing Zr and Ta contents on mechanical properties and also on precipitation of secondary phases during aging treatment was observed.
Anotace česky
výzkum je zaměřen na termomechanické ovlivnění slitin titanu.