J 2012

On the limitary radius of garnet structure compounds Y3Al5-xMxO12 (M = Cr, Co, Mn, Ni, Cu) and Y3Fe5-xCoxO12 (0 <= x <= 2.75) synthesized by sol-gel method

SKAUDŽIUS, Ramúnas, Jiří PINKAS, R. RAUDONIS, A. SELSKIS, R. JUSKENAS et. al.

Základní údaje

Originální název

On the limitary radius of garnet structure compounds Y3Al5-xMxO12 (M = Cr, Co, Mn, Ni, Cu) and Y3Fe5-xCoxO12 (0 <= x <= 2.75) synthesized by sol-gel method

Autoři

SKAUDŽIUS, Ramúnas (440 Litva), Jiří PINKAS (203 Česká republika, garant, domácí), R. RAUDONIS (440 Litva), A. SELSKIS (440 Litva), R. JUSKENAS (440 Litva) a Aivaras KAREIVA (440 Litva)

Vydání

Materials Chemistry and Physics, Lausenne, Elsevier Science SA, 2012, 0254-0584

Další údaje

Jazyk

angličtina

Typ výsledku

Článek v odborném periodiku

Obor

10402 Inorganic and nuclear chemistry

Stát vydavatele

Švýcarsko

Utajení

není předmětem státního či obchodního tajemství

Odkazy

Impakt faktor

Impact factor: 2.072

Kód RIV

RIV/00216224:14740/12:00066274

Organizační jednotka

Středoevropský technologický institut

UT WoS

000309247500035

Klíčová slova anglicky

Ceramics oxides; Sol-gel growth; Powder diffraction; Crystal structure

Štítky

Příznaky

Mezinárodní význam, Recenzováno
Změněno: 8. 4. 2014 11:58, Mgr. Nikola Kostlánová, Ph.D.

Anotace

V originále

The sinterability and microstructural evolution of mixed-metal Y3Al5-xCrxO12 (YACRG), Y3Al5-xMnxO12 (YAMNG), Y3Al5-xNixO12 (YANIG), Y3Al5-xCoxO12 (YACOG), Y3Al5-xCuxO12 (YACUG) and Y3Fe5-xCoxO12 (YICOG) (0 <= x <= 2.75) garnets powders, synthesized by an aqueous sol-gel process, were investigated. The synthesized samples were characterized by infrared spectroscopy (IR) and X-ray diffraction (XRD). Scanning electron microscopy (SEM) was used to study the morphology and microstructure of the synthesized samples. It was demonstrated, for the first time to the best our knowledge that the formation of YACRG, YAMNG, YANIG and YACOG garnets proceeds only within narrow substitutional range. Considerably less substitutional limit was observed for the YACUG garnet. On the other hand, the formation of monophasic YICOG garnet did not proceed at the same synthesis conditions. Furthermore, the limitary radius of garnet structure compounds was calculated. It was found that the linear dependence of the radius of M3+ cations distributed among tetrahedral and octahedral sites versus value of the limitary radius of garnet structure compounds exists.

Návaznosti

ED1.1.00/02.0068, projekt VaV
Název: CEITEC - central european institute of technology
GAP207/11/0555, projekt VaV
Název: Oxidy a fosforečnany kovů jako formy jaderného odpadu: studium sonochemického srážení, tepelných přeměn a rozpustnosti (Akronym: OPNW)
Investor: Grantová agentura ČR, Oxidy a fosforečnany kovů jako formy jaderného odpadu: studium sonochemického srážení, tepelných přeměn a rozpustnosti
MSM0021622410, záměr
Název: Fyzikální a chemické vlastnosti pokročilých materiálů a struktur
Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Fyzikální a chemické vlastnosti pokročilých materiálů a struktur