@proceedings{1122846, author = {Vašina, Petr and Žemlička, Radek and Buršíková, Vilma and Souček, Pavel and Vogel, Petr and Jílek, Mojmír}, booktitle = {IVC-19/ICSS-15 and ICN+T 2013}, keywords = {magnetron sputtering; TiC; cylindrical magnetron}, language = {eng}, title = {TF-P2-17 Preparation of Hard nc-TiC/a-C:H Coatings Using Hybrid PVD-PECVD Process with Rotating Cylindrical Magnetron}, year = {2013} }
TY - CONF ID - 1122846 AU - Vašina, Petr - Žemlička, Radek - Buršíková, Vilma - Souček, Pavel - Vogel, Petr - Jílek, Mojmír PY - 2013 TI - TF-P2-17 Preparation of Hard nc-TiC/a-C:H Coatings Using Hybrid PVD-PECVD Process with Rotating Cylindrical Magnetron KW - magnetron sputtering KW - TiC KW - cylindrical magnetron N2 - Hybrid PVD-PECVD process of titanium sputtering in a mixture of argon and acetylene combines aspects of both conventional techniques: sputtering of a rotating cylindrical titanium sputtering target (target size: 110 x 510 mm) by DC power and deposition from plasma activated acetylene which acts as a source of carbon for polymerization (PECVD). Titanium carbide/carbon nanocomposite hard coatings, which consist of TiC nanocrystallites embedded in amorphous carbon matrix (nc-TiC/a-C:H coating), were deposited on high speed steel and tungsten carbide cermet substrates which were placed on a DC biasable holder performing complex rotation around the Ti cathode. nc-TiC/a-C:H coatings with varying chemical composition prepared at 10 kW DC power (320 C), 20 kW (450 C) and 30 kW (450 C) and bias of -100 V reached maximal hardness of 24 GPa, 37 GPa and 28 GPa respectively. Because it could be expected that the optimal composition of the coating leading to maximal hardness should be reached independently on the applied power a process study was performed. Ti/Ar line intensity and discharge voltage showed sudden drop at the conditions where the maximal hardness was reached. EDX analyses show also sudden drop in Ti atomic concentration at this moment. ER -
VAŠINA, Petr, Radek ŽEMLIČKA, Vilma BURŠÍKOVÁ, Pavel SOUČEK, Petr VOGEL a Mojmír JÍLEK. TF-P2-17 Preparation of Hard nc-TiC/a-C:H Coatings Using Hybrid PVD-PECVD Process with Rotating Cylindrical Magnetron. In \textit{IVC-19/ICSS-15 and ICN+T 2013}. 2013.
|