SOUČEK, Pavel, Tereza SCHMIDTOVÁ, Vilma BURŠÍKOVÁ, Petr VAŠINA, Y.T. PEI, J.Th.M. DE HOSSON, Ondřej CAHA, Vratislav PEŘINA, Romana MIKŠOVÁ a Petr MALINSKÝ. Tribological properties of nc-TiC/a-C:H coatings prepared by magnetron sputtering at low and high ion bombardment of the growing film. Surface & coatings technology, Elsevier, 2014, roč. 241, February, s. 64-73. ISSN 0257-8972. doi:10.1016/j.surfcoat.2013.10.026.
Další formáty:   BibTeX LaTeX RIS
Základní údaje
Originální název Tribological properties of nc-TiC/a-C:H coatings prepared by magnetron sputtering at low and high ion bombardment of the growing film
Autoři SOUČEK, Pavel (203 Česká republika, domácí), Tereza SCHMIDTOVÁ (203 Česká republika, domácí), Vilma BURŠÍKOVÁ (203 Česká republika, domácí), Petr VAŠINA (203 Česká republika, garant, domácí), Y.T. PEI (528 Nizozemsko), J.Th.M. DE HOSSON (528 Nizozemsko), Ondřej CAHA (203 Česká republika, domácí), Vratislav PEŘINA (203 Česká republika), Romana MIKŠOVÁ (203 Česká republika) a Petr MALINSKÝ (203 Česká republika).
Vydání Surface & coatings technology, Elsevier, 2014, 0257-8972.
Další údaje
Originální jazyk angličtina
Typ výsledku Článek v odborném periodiku
Obor Fluids and plasma physics
Stát vydavatele Švýcarsko
Utajení není předmětem státního či obchodního tajemství
Impakt faktor Impact factor: 1.998
Kód RIV RIV/00216224:14310/14:00073503
Organizační jednotka Přírodovědecká fakulta
Doi http://dx.doi.org/10.1016/j.surfcoat.2013.10.026
UT WoS 000333000700014
Klíčová slova anglicky Nanocomposites; Magnetron sputtering; Titanium carbide; Ion flux; friction; wear
Štítky AKR, rivok
Příznaky Mezinárodní význam, Recenzováno
Změnil Změnila: doc. RNDr. Vilma Buršíková, Ph.D., učo 2418. Změněno: 15. 3. 2018 11:02.
Anotace
Two series of nc-TiC/a-C:H coatings were deposited by a hybridPVD – PECVD process of titanium sputtering in argon/ acetylene atmosphere at two configurations of magnetic field resulting in different impinging ion fluxes on the growing film. The composition of the coatings wasv aried by changing the acetylene gas flow during the depositions. Tribological tests were performed under conditions of emulating dry machining using 100Cr6 steel ball and silicon nitride ball as sliding counterparts. High temperature tribo-tests at 300 degC and 500 degC were performed with silicon nitride ball counterpart to examine the thermal stability of the coatings deposited at 320 degC. Special attention was paid to design coatings with optimal chemical composition for high hardness. The coef fi cient of friction (CoF) and wear as a function of C/Ti are presented. It is observed that in the range of 1 < C/Ti b < the CoF is largely independent of the ion flux during the deposition and is ~0.2 – 0.3. The CoF then decreases with increasing carbon content up to a certain limit. Highest carbon-containing coating shows an increased CoF and wear. The coatings became strongly oxidized after the high temperature test. The CoF for coa tings in the high hardness region is stable around 0.3 for the whole test at 300 degC, the CoF at 500 degC was stable at ~0.2 for the fi rst half of the test, and then the coating failed. The coating in the wear tracks was mostly delaminated.
Návaznosti
ED2.1.00/03.0086, projekt VaVNázev: Regionální VaV centrum pro nízkonákladové plazmové a nanotechnologické povrchové úpravy
GD104/09/H080, projekt VaVNázev: Plazmochemické procesy a jejich technologické aplikace
Investor: Grantová agentura ČR, Doktorské granty
MSM0021622411, záměrNázev: Studium a aplikace plazmochemických reakcí v neizotermickém nízkoteplotním plazmatu a jeho interakcí s povrchem pevných látek
Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Výzkumné záměry
VytisknoutZobrazeno: 23. 8. 2019 16:27