SOUČEK, Pavel, Josef DANIEL, Jaroslav HNILICA, Katarína BERNÁTOVÁ, Lukáš ZÁBRANSKÝ, Vilma BURŠÍKOVÁ, Monika STUPAVSKÁ a Petr VAŠINA. Superhard nanocomposite nc-TiC/a-C:H coatings: The effect of HiPIMS on coating microstructure and mechanical properties. Surface & coatings technology. Lausanne: Elsevier Science, 2017, roč. 311, February, s. 257-267. ISSN 0257-8972. doi:10.1016/j.surfcoat.2017.01.021.
Další formáty:   BibTeX LaTeX RIS
Základní údaje
Originální název Superhard nanocomposite nc-TiC/a-C:H coatings: The effect of HiPIMS on coating microstructure and mechanical properties
Autoři SOUČEK, Pavel (203 Česká republika, domácí), Josef DANIEL (203 Česká republika, domácí), Jaroslav HNILICA (203 Česká republika, domácí), Katarína BERNÁTOVÁ (703 Slovensko, domácí), Lukáš ZÁBRANSKÝ (203 Česká republika, domácí), Vilma BURŠÍKOVÁ (203 Česká republika, domácí), Monika STUPAVSKÁ (703 Slovensko, domácí) a Petr VAŠINA (203 Česká republika, garant, domácí).
Vydání Surface & coatings technology, Lausanne, Elsevier Science, 2017, 0257-8972.
Další údaje
Originální jazyk angličtina
Typ výsledku Článek v odborném periodiku
Obor 10305 Fluids and plasma physics
Stát vydavatele Švýcarsko
Utajení není předmětem státního či obchodního tajemství
WWW URL
Impakt faktor Impact factor: 2.906
Kód RIV RIV/00216224:14310/17:00096014
Organizační jednotka Přírodovědecká fakulta
Doi http://dx.doi.org/10.1016/j.surfcoat.2017.01.021
UT WoS 000395355300030
Klíčová slova anglicky http://dx.doi.org/10.1016/j.surfcoat.2017.01.021
Štítky NZ, rivok
Příznaky Mezinárodní význam, Recenzováno
Změnil Změnila: Ing. Nicole Zrilić, učo 240776. Změněno: 12. 4. 2018 10:03.
Anotace
Nanocomposite coatings consisting of titanium carbide crystallites embedded in amorphous carbon matrix were deposited utilizing direct current magnetron sputtering (DCMS) and high power impulse magnetron sputtering (HiPIMS) of titanium target in argon/acetylene atmosphere. DC driven depositions of coatings with high amount of carbon were accompanied by significant arcing during the deposition. HiPIMS utilization made reliable arc-free deposition of coatings with high carbon content possible. Analyses of the coating structure revealed that utilization of HiPIMS favours carbon incorporation into the TiCx grains rather than to the matrix. HiPIMS deposited coatings exhibited stoichiometry of the TiCx grains closer to unity with grains exhibiting lower lattice parameter and a lower fraction of the a-C matrix. This led to a smaller mean TiCx grain separation by the a-C:H matrix. Also the surface structure of the HiPIMS deposited coatings was much finer. The structure refinement resulted in overall higher hardness of HiPIMS deposited coatings with the hardest coatings reaching the superhard region of > 40 GPa and in 40% increase of H/E ratio and nearly threefold increase of H3/E2 ratio.
Návaznosti
LO1411, projekt VaVNázev: Rozvoj centra pro nízkonákladové plazmové a nanotechnologické povrchové úpravy (Akronym: CEPLANT plus)
Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Národní program udržitelnosti I (LO)
VytisknoutZobrazeno: 10. 5. 2021 01:26