Thermal stability of fracture-resistant W-B-C coatings

MIRZAEI, Saeed; Pavel SOUČEK; Lukáš ZÁBRANSKÝ; Mostafa ALISHAHI; Vilma BURŠÍKOVÁ et al.

Základní údaje

Originální název

Thermal stability of fracture-resistant W-B-C coatings

Autoři

MIRZAEI, Saeed; Pavel SOUČEK; Lukáš ZÁBRANSKÝ; Mostafa ALISHAHI; Vilma BURŠÍKOVÁ a Petr VAŠINA

Vydání

Reactive Sputter Deposition, RSD 2019, 2019

Další údaje

Jazyk

angličtina

Typ výsledku

Konferenční abstrakt

Stát vydavatele

Německo

Utajení

není předmětem státního či obchodního tajemství

Označené pro přenos do RIV

Ne

Organizační jednotka

Přírodovědecká fakulta

Klíčová slova česky

Magnetron Sputtering, Coating, Thermal stability, WBC

Klíčová slova anglicky

Magnetron Sputtering, Coating, Thermal stability, WBC

Příznaky

Recenzováno
Změněno: 22. 6. 2020 17:43, Saeed Mirzaei, Ph.D., M.Sc.

Anotace

V originále

Recently, several studies have documented the potential applications of W-B-C coatings with enhanced mechanical properties in the tooling industry. Such applications often require a high thermal stability due to exposure of the material to high temperatures. Here, thermal stability of magnetron sputtered W-B-C coatings up to 1100 °C was investigated after both conventional furnace annealing and RTA methods. The microstrcural changes and mechanical behavior upon annealing were studied. As-deposited coatings exhibited a nearly amorphous character with a preserved microstructure and surface morphology until 900 °C while after annealing to 1100 °C, a strong crystallization was observed. The formation of WB, W2B, WC and W2C after conventional annealing and WB, WC and W2B after RTA was suggested by XRD. Cobalt atoms were diffused into the porous coating with a columnar growth to form CoWB phase. The high-resolution XPS scans revealed a dominant fraction of W−B bonds after RTA treatment. Mechanical properties were mostly affected by chemical composition and developed phases during annealing. Fracture resistance of the coating was generally decreased after annealing to 1100 °C. No oxidation layer was observed on the coating, even after storage for one year, which suggests that W-B-C coating with high oxidation resistance.

Návaznosti

GA15-17875S, projekt VaV
Název: Lokální mikrostrukturní změny vyvolané statickou a dynamickou indentací nanostrukturovaných a nanolaminovaných povlaků
Investor: Grantová agentura ČR, Lokální mikrostrukturní změny vyvolané statickou a dynamickou indentací nanostrukturovaných a nanolaminovaných povlaků
LO1411, projekt VaV
Název: Rozvoj centra pro nízkonákladové plazmové a nanotechnologické povrchové úpravy (Akronym: CEPLANT plus)
Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Rozvoj centra pro nízkonákladové plazmové a nanotechnologické povrchové úpravy