Effect of Gd addition on the structural and magnetic properties of L10-FePt alloy thin films
SCHMIDT, Nataliia Y., Sukhrob ABDULAZHANOV, Jan MICHALIČKA, Julian HINTERMAYR, Ondřej MAN et. al.Základní údaje
Originální název
Effect of Gd addition on the structural and magnetic properties of L10-FePt alloy thin films
Autoři
SCHMIDT, Nataliia Y., Sukhrob ABDULAZHANOV, Jan MICHALIČKA, Julian HINTERMAYR (garant), Ondřej MAN, Ondřej CAHA (203 Česká republika, domácí), Michal URBÁNEK a Manfred ALBRECHT
Vydání
Journal of Applied Physics, AIP Publishing, 2022, 0021-8979
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10300 1.3 Physical sciences
Stát vydavatele
Spojené státy
Utajení
není předmětem státního či obchodního tajemství
Odkazy
Impakt faktor
Impact factor: 3.200
Kód RIV
RIV/00216224:14310/22:00128349
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000894312900001
Klíčová slova anglicky
anisotropy; fept films
Štítky
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 30. 1. 2023 09:19, Mgr. Marie Šípková, DiS.
Anotace
V originále
The impact of Gd addition on the structural and magnetic properties of 𝐿10-FePt alloy thin films, which were sputter-deposited on MgO(001) substrates at 800∘C, was investigated. A rapid deterioration of 𝐿10 chemical ordering along with a strong amorphization effect is observed with addition of Gd. At more than 20 at. % Gd, additional crystalline phases occur. Due to the diminishing 𝐿10 chemical order, the perpendicular magnetic anisotropy (PMA) gets strongly reduced from about 3 down to 1 MJ/m3 with addition of 14 at. % Gd. For higher Gd concentrations, the easy axis of magnetization turns fully in-plane due to dominating magnetic shape anisotropy. Furthermore, the saturation magnetization gets reduced with Gd addition due to the antiferromagnetic coupling between the Fe and Gd magnetic moments. Also, the Curie temperature can be lowered. Interestingly, with addition of Gd, a change in film morphology takes place, changing from an isolated island structure to a more continuous film morphology, which is of particular interest for samples with low Gd concentration as these films exhibit still strong PMA but rather low coercive fields.