Carbon nanostructures synthesis in microwave plasma torch at atmospheric pressure

JAŠEK, Ondřej, Marek ELIÁŠ, Lenka ZAJÍČKOVÁ, Zuzana KUČEROVÁ, Jiřina MATĚJKOVÁ, Antonín REK a Jiří BURŠÍK. Carbon nanostructures synthesis in microwave plasma torch at atmospheric pressure. In Book of Abstracts 3rd International conference on microwave chemistry. 1. vyd. Brno: Masaryk University. s. PO-7, 1 s. ISBN 80-210-4070-X. 2006.

Základní údaje

• Originální název: Carbon nanostructures synthesis in microwave plasma torch at atmospheric pressure
• Název česky: Depozice uhlíkových nanostruktur v mikrovlnném výboji za atmosférického tlaku
• Název anglicky: Carbon nanostructures synthesis in microwave plasma torch at atmospheric pressure
• Autoři: JAŠEK, Ondřej (203 Česká republika, garant), Marek ELIÁŠ (203 Česká republika), Lenka ZAJÍČKOVÁ (203 Česká republika), Zuzana KUČEROVÁ (203 Česká republika), Jiřina MATĚJKOVÁ (203 Česká republika), Antonín REK (203 Česká republika) a Jiří BURŠÍK (203 Česká republika).
• Vydání: 1. vyd. Brno, Book of Abstracts 3rd International conference on microwave chemistry, od s. PO-7, 1 s. 2006.
• Nakladatel: Masaryk University

Další údaje

• Originální jazyk: čeština
• Typ výsledku: Stať ve sborníku
• Obor: 10305 Fluids and plasma physics
• Stát vydavatele: Česká republika
• Utajení: není předmětem státního či obchodního tajemství
• Kód RIV: RIV/00216224:14310/06:00028950
• Organizační jednotka: Přírodovědecká fakulta
• ISBN: 80-210-4070-X
• Klíčová slova anglicky: carbon nanostructures; atmospheric pressure; microwave discharge; electron microscopy
• Štítky: atmospheric pressure, carbon nanostructures, electron microscopy, microwave discharge

Anotace

We have successfully synthesized CNTs in microwave plasma torch at atmospheric pressure from the mixture of methane, hydrogen and argon. The plasma torch was generated at the frequency of 2.45 GHz using an iron hollow electrode. Argon (1000 sccm) was flowing through the electrode whereas methane (10-40 sccm) and hydrogen (100-400 sccm) were added to the expanding torch from outside. The CNTs were grown on substrates placed at various distances from the torch electrode. The substrates were silicon wafers(10x15 mm) with deposited 200 nm thick silicon oxide layer and thin layer (5-20 nm) of iron catalyst on the top. The samples were imaged by scanning electron microscopy(SEM) and transmission electron microscopy(TEM). The processes in the discharge were monitored by optical emission spectroscopy(OES). The SEM analysis showed presence of well aligned 50 micrometer long multi-wall CNTs with narrow diameter distribution centered around 20 nm. Except the carbon nanotubes the layers often contained various carbon and carbon/iron structures.

Anotace anglicky

We have successfully synthesized CNTs in microwave plasma torch at atmospheric pressure from the mixture of methane, hydrogen and argon. The plasma torch was generated at the frequency of 2.45 GHz using an iron hollow electrode. Argon (1000 sccm) was flowing through the electrode whereas methane (10-40 sccm) and hydrogen (100-400 sccm) were added to the expanding torch from outside. The CNTs were grown on substrates placed at various distances from the torch electrode. The substrates were silicon wafers(10x15 mm) with deposited 200 nm thick silicon oxide layer and thin layer (5-20 nm) of iron catalyst on the top. The samples were imaged by scanning electron microscopy(SEM) and transmission electron microscopy(TEM). The processes in the discharge were monitored by optical emission spectroscopy(OES). The SEM analysis showed presence of well aligned 50 micrometer long multi-wall CNTs with narrow diameter distribution centered around 20 nm. Except the carbon nanotubes the layers often contained various carbon and carbon/iron structures.

Návaznosti

• GA202/05/0607, projekt VaV: Název: Příprava uhlíkových mikro- a nanostruktur plazmovými technologiemi

Investor: Grantová agentura ČR, Příprava uhlíkových mikro- a nanostruktur plazmovými technologiemi

• MSM0021622411, záměr: Název: Studium a aplikace plazmochemických reakcí v neizotermickém nízkoteplotním plazmatu a jeho interakcí s povrchem pevných látek

Investor: Ministerstvo školství, mládeže a tělovýchovy ČR, Studium a aplikace plazmochemických reakcí v neizotermickém nízkoteplotním plazmatu a jeho interakcí s povrchem pevných látek