Evaluation of composition, mechanical properties and structure of nc-TiC/a-C:H coatings prepared by balanced magnetron sputtering
SOUČEK, Pavel, Tereza SCHMIDTOVÁ, Lukáš ZÁBRANSKÝ, Vilma BURŠÍKOVÁ, Petr VAŠINA et. al.Základní údaje
Originální název
Evaluation of composition, mechanical properties and structure of nc-TiC/a-C:H coatings prepared by balanced magnetron sputtering
Autoři
SOUČEK, Pavel (203 Česká republika, domácí), Tereza SCHMIDTOVÁ (203 Česká republika, domácí), Lukáš ZÁBRANSKÝ (203 Česká republika, domácí), Vilma BURŠÍKOVÁ (203 Česká republika, garant, domácí), Petr VAŠINA (203 Česká republika, domácí), Ondřej CAHA (203 Česká republika, domácí), Mojmír JÍLEK (203 Česká republika), Abdelazziz EL MEL (250 Francie), Pierre-Yves TESSIER (250 Francie), Jan SCHÄFER (203 Česká republika), Jiří BURŠÍK (203 Česká republika), Vratislav PEŘINA (203 Česká republika) a Romana MIKŠOVÁ (203 Česká republika)
Vydání
Surface & Coatings Technology, Elsevier Science, 2012, 0257-8972
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10305 Fluids and plasma physics
Stát vydavatele
Švýcarsko
Utajení
není předmětem státního či obchodního tajemství
Odkazy
Impakt faktor
Impact factor: 1.941
Kód RIV
RIV/00216224:14310/12:00057246
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000313919500024
Klíčová slova anglicky
Carbon; Magnetron sputtering; Mechanical properties; Nanocomposite; Titanium
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 22. 7. 2024 10:15, Mgr. Marie Šípková, DiS.
Anotace
V originále
Nanocomposites like nc-TiC/a-C:H show promising combinations of properties such as high hardness and Young's modulus combined with low friction and wear. These properties can be furthermore tailored to suit particular industrial needs. In this paper, we report on the preparation and analyses of several um thick and well adherent nc-TiC/a-C:H coatings with different stoichiometry. These coatings were deposited in a relatively low ion bombardment environment using magnetron sputtering of titanium target operated in well-balanced magnetic field configuration on high speed steel and hardmetal substrates. Gaseous hydrocarbon (acetylene) was added to the deposition chamber as source of carbon. Hardness and Young's modulus of 46 GPa and 415 GPa respectively were reached.