Study of alumosilicate porcelains: Sol-gel preparation, characterization and erosion evaluated by gravimetric method
BOGDANOVICIENE, Irma, Audrone JANKEVICIUTE, Jiří PINKAS, Aldona BEGANSKIENE, Aivaras KAREIVA et. al.Základní údaje
Originální název
Study of alumosilicate porcelains: Sol-gel preparation, characterization and erosion evaluated by gravimetric method
Název česky
Studium aluminosilikátových porcelánů: Příprava sol-gelovou metodou, charakterizace a hodnocení eroze gravimetrickou metodu
Autoři
BOGDANOVICIENE, Irma (440 Litva), Audrone JANKEVICIUTE (440 Litva), Jiří PINKAS (203 Česká republika, garant), Aldona BEGANSKIENE (440 Litva) a Aivaras KAREIVA (440 Litva)
Vydání
Materials Research Bulletin, Elsevier, 2008, 0025-5408
Další údaje
Jazyk
angličtina
Typ výsledku
Článek v odborném periodiku
Obor
10402 Inorganic and nuclear chemistry
Stát vydavatele
Nizozemské království
Utajení
není předmětem státního či obchodního tajemství
Impakt faktor
Impact factor: 1.812
Kód RIV
RIV/00216224:14310/08:00024933
Organizační jednotka
Přírodovědecká fakulta
UT WoS
000260292400021
Klíčová slova anglicky
Ceramics; Inorganic compounds; Oxides; Sol-gel chemistry
Štítky
Příznaky
Mezinárodní význam, Recenzováno
Změněno: 3. 9. 2010 15:45, prof. RNDr. Jiří Pinkas, Ph.D.
V originále
In this paper, the sol gel synthesis and characteristic properties of kalsilite type alumosilicates (KAlSiO4 and K0.5Na0.5AlSiO4) are reported. The polycrystalline powders were characterized by thermal analysis (TG/DTA), powder X ray diffraction analysis (XRD) and scanning electron microscopy (SEM). Single phase kalsilite oxides have been obtained after annealing precursor gels for 5 h in the temperature range of 750 to 850 C. It was demonstrated that crystallinity of the samples slightly depends on the temperature of annealing. From the results obtained, it could be concluded that the KAlSiO4 solids are composed of the volumetric plate like grains with no regular size (from 5 to 30 microm at 750 C and around 5 to 50 microm at 850 C). Larger crystallites for mixed potassium sodium kalsilite have formed (from 10 to 80 microm at 750 C and above 100 microm at 850 C) in comparison with potassium kalsilite samples). The erosion of obtained dental porcelain samples stored in saliva, beer and CocaCola was compared.
Česky
Byla provedena sol-gelová příprava a charakterizace vlastností aluminosilikátů kalsilitového typu (KAlSiO4 a K0.5Na0.5AlSiO4). Polykrystalické prášky byly charakterizovány pomocí termické analýzy (TG/DTA), rtg. práškové difrakce (XRD) a skenovací elektronové mikroskopie (SEM). Monofázické kalsilitové oxidy byly získány zahřívaním prekurzorních gelů 5 h na 750 až 850 oC. Krystalinita produktů závísí na kalcinační teplotě.